Optimization of Iron Oxide (Fe2O3) Addition Parameters on the Physical Properties of Al-Si Alloys as an Advanced Material Innovation
DOI:
https://doi.org/10.26905/jtmt.v20i2.13908Keywords:
Al-Si, Phiysical Properties, TaguchiAbstract
Aluminum-silicon alloys are widely used in the industrial world, one of which is because they have high wear resistance. The aim of this research is to determine the physical and mechanical properties of the Al-Si alloy after strengthening by mixing reinforcing materials. The research method uses Taguchi optimization and analysis of the physical properties of the Al-Si alloy test results. The results showed that the highest hardness value was obtained in the 7th experiment, namely with a rotation variation of 2000 rpm, temperature of 6000C, and holding time of 60 seconds. This result is in line with the results of the tensile strength test, where the highest tensile strength was also obtained in the 7th experiment. This result is supported by the results of other researchers, which show that the higher the rotation in the casting results in higher hardness. The results of the microphotographs show that all alloy materials have an even distribution of grains, the grain size appears small, and the dendrites in the raw Al-Si alloy appear small compared to other materials. The macro photo results show that all alloy materials have fractures that appear brittle, as evidenced by the fact that these fractures provide light reflection.
References
E. Darezereshki, F. Bakhtiari, and M. Alizadeh, “Direct thermal decomposition synthesis and characterization,†Mater. Sci. Semicond. Process., vol. 15, no. 1, pp. 91–97, 2012, doi: 10.1016/j.mssp.2011.09.009.
M. M. Haque and A. Sharif, “Study on wear properties of aluminium – silicon piston alloy,†vol. 118, pp. 69–73, 2001.
M. M. Haque and M. A. Maleque, “Effect of process variables on structure and properties of aluminium – silicon piston alloy,†vol. 77, pp. 122–128, 1998.
S. Nayak and A. Karthik, “Synthesis Of Al-Si Alloys And Study Of Their Mechanical Properties Bachelor of Technology Synthesis Of Al-Si Alloys And Study Of Their Mechanical Properties Bachelor of Technology,†pp. 1–61, 2011.
G. Frederic, V. Voort, J. Asensio-lozano, and J. Asension-lozano, “The Al-Si Phase Diagram The Al-Si Phase Diagram,†no. January 2018, 2009, doi: 10.1017/S1431927609092642.
D. I. Tsamroh, P. Puspitasari, A. Andoko, A. A. Permanasari, and P. E. Setyawan, “Optimization of multistage artificial aging parameters on Al-Cu alloy mechanical properties,†J. Achiev. Mater. Manuf. Eng., vol. 87, no. 2, pp. 62–67, 2018, doi: 10.5604/01.3001.0012.2828.
J. T. O. Florenciano, A. Ambrosi, D. Hotza, and S. Y. G. González, “Understanding centrifugal casting in the manufacture of functionally graded materials,†J. Eur. Ceram. Soc., vol. 42, no. 15, pp. 7089–7101, 2022, doi: 10.1016/j.jeurceramsoc.2022.08.042.
W. Callister and D. Rethwisch, Materials science and engineering: an introduction. 2015. doi: 10.1016/0025-5416(87)90343-0.
D. M. Wibisono, A. Suprapto, D. I. T. Jumiadi, and ..., “Analisis Hasil Pengecoran Sentrifugal dengan Variasi Kecepatan Putaran (Rpm) Material Aluminium 6061 Menggunakan Mesin Prototipe Pengecoran …,†… Fak. Tek. 2021, pp. 103–114, 2021.
S. G. Shabestari, “The effect of iron and manganese on the formation of intermetallic compounds in aluminum – silicon alloys,†vol. 383, pp. 289–298, 2004, doi: 10.1016/j.msea.2004.06.022.
J. A. Taylor, “The Effect of Iron in Al-Si Casting Alloys,†no. October 2004, 2016.
M. A. Moustafa, “Effect of iron content on the formation of ⤠-Al 5 FeSi and porosity in Al – Si eutectic alloys,†vol. 9, no. 1995, pp. 605–610, 2008, doi: 10.1016/j.jmatprotec.2008.02.073.
J. A. Taylor, “Iron-containing intermetallic phases in Al-Si based casting alloys,†vol. 1, pp. 19–33, 2012, doi: 10.1016/j.mspro.2012.06.004.
M. Timpel, N. Wanderka, R. Schlesiger, T. Yamamoto, N. Lazarev, and D. Isheim, “The role of strontium in modifying aluminium – silicon alloys,†Acta Mater., vol. 60, no. 9, pp. 3920–3928, 2012, doi: 10.1016/j.actamat.2012.03.031.
S. Patra, “Microstructure and Mechanical Property of Al-Si Alloy,†Res. Gste, no. April, pp. 1–16, 2016, doi: 10.13140/RG.2.1.1604.9043.
O. A. Sastranegara, “Mengenal Uji Tarik dan Sifat-sifat Mekanik Logam,†pp. 1–6, 2013.
H. H. Knowl Piece, Wilbury Way, “Introduction to Tensile Testing,†ASM Int., pp. 1–13, 2004.
P. Puspitasari and A. Khafiddin, “Analisis Hasil Pengecoran Logam Al-Si Menggunakan Lumpur Lapindo Sebagai Pengikat Pasir Cetak,†no. 2, pp. 1–11, 2014.
J. F. Su, “Characterization of Fracture and Debonding of Silicon Particles in Aluminium Silicon Alloys,†pp. 1–110, 2009.
Downloads
Published
Issue
Section
License
This work, is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish with this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License. that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.
- Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) before and during the submission process, as it can lead to productive exchanges and earlier and greater citation of published work.